SS Buildcare

Araldite®AW 106 / Hardener HV 953 UTwo component epoxy paste adhesiveKey propertiesMulti purposeLong working life Low shrinkageGood resistance to dynamic loadingBonds a wide variety of materials in common useDescriptionAraldite®AW106/HardenerHV953Uisamultipurpose,twocomponent,roomtemperaturecuring,pasteadhesiveof high strength and toughness.Itissuitableforbondingawidevarietyofmetals,ceramics,glass,rubber,rigidplasticsandmostothermaterialsincommon use. It is a versatile adhesive for the craftsman as well as most industrial applications.

Sikament®-2001 NS A plasticizer which imparts high workability and gives workability retention. USES Sikament®-2001 NS a plasticizer for free flowing concrete in floor, slabs, foundations, slender components with dense reinforcement, walls, columns, pavements and other structural and non structural elements. Specially recommended for the following types of concrete: ▪ Ready mix concrete ▪ Pre cast concrete ▪ Site batched concrete CHARACTERISTICS / ADVANTAGES Sikament®-2001 NS produces a more uniformly cohesive high quality free flowing concrete. It has following advantages : ▪ Improved strength and density ▪ Improved consistence retention ▪ Improved durability ▪ Improved water tightness ▪ Improved surface finish ▪ Improved cohesion properties APPROVALS / STANDARDS IS 9103-1999, ASTM C494

Mainly with liquid epoxy resins such as Araldite GY 250, PY 720, GY 783 for solventfree or heavy-filled mastics, epoxy resin mortars or reaction adhesives. For application to steel or mineral substrates.

WE ARE DEAL IN ALL ARALDITE PRODUCT WHICH MAKES HUAraldite®AW 106 / Hardener HV 953 UTwo component epoxy paste adhesiveKey propertiesMulti purposeLong working life Low shrinkageGood resistance to dynamic loadingBonds a wide variety of materials in common useDescriptionAraldite®AW106/HardenerHV953Uisamultipurpose,twocomponent,roomtemperaturecuring,pasteadhesiveof high strength and toughness.Itissuitableforbondingawidevarietyofmetals,ceramics,glass,rubber,rigidplasticsandmostothermaterialsincommon use. It is a versatile adhesive for the craftsman as well as most industrial applications.NTSMAN, ALL TYPE ADHESIVE. 

Measure (by weight or volume) the Araldite resin and the hardener. Add the hardener to the Araldite resin; making sure that the required amount of hardener is transferred to the resin. Stir thoroughly until mixing is complete. Air entrainment during mixing results in pores in the cured resin. Mixing under vacuum or in a metering-mixing machine is the most effective way to prevent air entrainment. Alternatively the static resin – hardener mixture may be deaerated in a vacuum chamber – allowing at least 200 % ullage for the foam to expand. Curing The chemical reaction initiated by mixing resin and hardener results in the generation of exothermic heat. The peak temperatures attained are determined by the starting temperature and the size and shape of the casting. Unfilled resin systems are suitable only for manufacturing castings weighing up to about 500 grams. Mineral filler should be added to dissipate heat and damp the exothermic reaction when producing large castings. There is very little exothermic reaction when producing very small castings or thin layers as the heat generated is rapidly dissipated. Cure is consequently delayed and the surfaces of castings may remain tacky. In such cases an infrared heater or oven at 40°C – 60°C should be used to effect full cure. 
The Araldite HY 951 Epoxy Hardener is mixed with epoxy resin for coating or encapsulating electronic components which work at low voltages. This hardener is a clear liquid with a flash point of 110 degrees centigrade, mix ratio 100:10 and specific gravity is 0.98 gm/cm3 at 25 degrees centigrade. The hardener is capable of producing medium-viscosity adhesives in order to bond ceramics, glasses, rubbers, plastics and other substrates. Mix this hardener with resin thoroughly at room temperature. You can easily apply this hardener over the large surfaces of substrates. The Araldite HY 951 Epoxy Hardener is admired for good resistivity against chemical & atmospheric conditions, excellent mechanical strength and better electrical properties.